HOME > PRODUCT > Material 


¢º Ni-Zn Materials

Material YN-201 YL-9N YL-81
Initial permeability(¥ìiac)   300¡¾20% 350¡¾20% 350¡¾20%
Saturation magnetic
flux density(Bs)
mT
 [H=1194A/m]
400 330 330
Remanent flux density(Br) mT 300 205 80
Coercive force(Hc) A/m 60 48 48
Relative loss factor(tan¥ä/¥ìi) X10-6 30 12 25
Relative temp. factor(¥á¥ìr)   X10-6/¡É 3~4 5 12
Curie temperature(Tc) ¡É >200 >170 >150
Electrical resistivity M¥Ø¡¤m >10 >10 >10
Density(d)  kg/§© 5.0¡¿10©ø 5.0¡¿10©ø 5.0¡¿10©ø
* Typical values
* The value were obtained with toroidal cores(25¡¿15¡¿5mm) at room temperature unless otherwise shown
 
 
Material YN-400 YN-800 YN-202
Initial permeability(¥ìiac)   300¡¾20% 800¡¾25% 1300¡¾20%
Saturation magnetic
flux density(Bs)
mT
[H=1194A/m]
420 360 360
Remanent flux density(Br) mT 160 220 170
Coercive force(Hc) A/m 35 20 18
Relative loss factor(tan¥ä/¥ìi) X10-6 8 21 25
Curie temperature(Tc) ¡É >200 ¡Ã170 ¡Ã160
Electrical resistivity M¥Ø¡¤m >10 >10 >10
Density(d) kg/§© 5.0¡¿10©ø 5.0¡¿10©ø 5.0¡¿10©ø
* Typical values
* The value were obtained with toroidal cores(25¡¿15¡¿5mm) at room temperature unless otherwise shown
 
 
Material YT-314 YH-20R  
Initial permeability(¥ìiac)   1000¡¾20% 2000¡¾20%  
Saturation magnetic
flux density(Bs)
mT
[H=1194A/m]
280 260  
Remanent flux density(Br) mT 130 100  
Coercive force(Hc) A/m 32 11  
Relative loss factor(tan¥ä/¥ìi) X10-6 15(0.1MHz) 25(0.1MHz)  
Relative temp. factor(¥á¥ìr) X10-6/¡É 2 3~4  
Curie temperature(Tc) ¡É >110 >100  
Electrical resistivity ¥Ø¡¤m >1.0 >1.0  
Density(d) kg/§© 5.0¡¿10©ø 4.9¡¿10©ø  

* Typical values
* The value were obtained with toroidal cores(25¡¿15¡¿5mm) at room temperature unless otherwise shown